Are you looking for a 7075 T651 aluminum sheet supplier in China? Contact with Yantai Edobo Aluminum Co.,Ltd, we will start a long-term business cooperation by this chance.
Specifications of 7075 T651 Aluminium Slug：
Aluminium Alloy Plate: 7075 T651
Temper: T6/ T651
Thickness: 5mm to 150mm,
Stock Size: 4 x 8; 1219 x 2438mm,1500mm x 3000mm; 1524mm x 3048mm
Produce to ASTM B209 or GB/T3880-2012, EN485 standard;
Surface: mill finish surface, bright, polished surface,
Over 3,000Tons ready stock with standard size 1524x 3048mm & 1500 x 3000mm
We can cut the corresponding size according to your needs
Cutting can be done using mechanical cutting tools such as shearing machines or cutting machines, according to the size requirements provided by the customer.
What will affect the cutting of aluminum alloy slugs？
1.Cutting process: Choosing the appropriate cutting process is crucial for obtaining high-quality aluminum plate cutting. Common cutting techniques include mechanical cutting, laser cutting, and plasma cutting. Each cutting process has its advantages and limitations. For example, laser cutting has high precision and a small heat affected zone, but may result in higher cutting costs.
2. Cutting speed: Cutting speed refers to the speed at which the cutting tool or cutting equipment moves during the cutting process. Cutting speeds that are too fast or too slow can affect cutting quality. If the cutting speed is too fast, it may cause burrs, slag residue, or uneven cutting lines on the cutting edge. On the contrary, a slow cutting speed may result in excessive heat generation during the cutting process, causing deformation of the aluminum plate or welding slag on the cutting line.
3.Material characteristics: The hardness, thickness, purity, and surface condition of aluminum plates can also affect cutting quality. Aluminum plates with higher hardness may require stronger cutting equipment and more wear-resistant cutting tools. Thicker aluminum plates may require more powerful cutting equipment to ensure cutting efficiency. Meanwhile, the flatness and smoothness of the surface state can also affect the accuracy and quality of cutting,
6061 Aluminum Plate Quality Data Sheet/Chemistry Composition:
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Single | Total | |||||||||||
7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | \ | 5.1-6.1 | 0.2 | 0.05 | 0.15 | remainder |
What is 7000 series aluminum alloy？
7xxx aluminum alloy
The main alloying element of Class 7 aluminum alloys is zinc, usually with a certain amount of copper and magnesium.
Due to the use of zinc, this type of alloy is the strongest among all forged alloys, and its strength can even exceed that of some steels.
That's why Class 7 alloys are commonly used in the aircraft industry. Although the addition of zinc can also reduce its processability, its excellent strength compensates for these drawbacks.
For example, 7075 aluminum alloy is an ideal choice for high stress parts due to its excellent weight to strength ratio. And it can be processed by molding, heat treatment and other operations as needed.
6061-T6 Aluminum Alloy Plate Mechanical Properties Standard：
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Hardness | |
|---|---|---|---|---|---|
| 7075 T6 | 525Mpa | 6 | Qualified | 157HB | |
| 7075 T651 | 540Mpa | 6 | Qualified | 160HB | |
What is 7075 T651 aluminum Sheet？
7075-T651 is known as the best product among aluminum alloys. T651 indicates that this alloy has undergone heat treatment and pre stretching processes. T6 and T651 alloys have a tensile strength of 572 MPa and a yield strength of 503 MPa. Meanwhile, 7075 alloy has excellent mechanical properties and anodizing performance. The American ASTM.
Standards Association evaluates 7075 alloy as having Class B mechanical properties due to its ability to produce curled or easily breakable chips and excellent surface treatment.
What are the applications of 7075 aluminum alloy?
When weight is a critical factor but strength cannot be compromised, the 7075 T651 aluminum plate is a widely favored alternative to steel. Alloy 7075 boasts an exceptional strength-to-weight ratio, far superior to that of steel, making it a popular choice across multiple industries. With a strength-to-weight ratio of 196 kN-m/kg, 7075 combines high strength and light weight, ideal for demanding sectors such as aviation, automotive, and firearms manufacturing.
Originally developed in 1936, 7075 was introduced as a solution to enhance aircraft fuel efficiency by reducing weight while maintaining the structural integrity required for complex maneuvers. Although it doesn't offer the same level of corrosion resistance as alloy 6061, its outstanding performance in high-stress environments, thanks to zinc being its primary alloying element, has cemented its role in the aerospace industry.
Beyond aviation, 7075 is also heavily utilized in the automotive industry for similar reasons, offering both durability and weight savings. Its strength has also made it a key material in the firearms industry, with the alloy featured in the construction of weapons like the M16, AR-15, and various handguns.
As a member of the 7000 aluminum series, 7075 is now integral to countless products in a variety of applications where high strength and reduced weight are essential.
1.How to use 7075 aluminum alloy
7075-T651 is a high-strength aluminum alloy commonly used to manufacture components that withstand high stress, such as aerospace parts, bicycle frames, etc. To ensure a flatness of 0.03 threads, precise processing techniques and equipment are required.
The following are possible processing techniques:
Precision cutting: Using high-precision CNC machine tools and rigid cutting tools, adopting a cutting method of small cutting depth, small feed rate, and low cutting speed to reduce the impact of cutting force on the workpiece and ensure flatness.
Grinding processing: High precision surface grinding machines or CNC grinding machines are used, with fine grinding wheels and coolant to control the temperature and pressure during the grinding process, ensuring grinding accuracy and flatness.
Grinding: Using grinding tools and abrasives, the surface roughness is removed through the grinding process to improve flatness.
Polishing: Using polishing cloth, polishing agent and other materials, the micro unevenness of the surface is removed by manual or mechanical polishing to improve flatness.
It should be noted that in order to ensure flatness and accuracy, the material needs to be accurately measured and calibrated before processing. During processing, environmental factors such as temperature and humidity need to be strictly controlled, and precise testing and inspection are required after processing.
2.7075 t651 Aluminum vs 7075-t7351 Aluminum
T651 is first subjected to solution treatment followed by artificial aging, and then subjected to tensile treatment to eliminate residual stress after solution treatment;
T7351 is subjected to graded aging after solution treatment, and is subjected to tensile treatment to eliminate residual stress after solution treatment. Its strength is lower than T651 and its corrosion resistance is significantly improved.
Contact us for the latest aluminum prices
Are you looking for a 7075 T651 aluminum sheet supplier in China? Contact with Yantai Edobo Aluminum Co.,Ltd, we will start a long-term business cooperation by this chance.
Specifications of 7075 T651 Aluminium Slug：
Aluminium Alloy Plate: 7075 T651
Temper: T6/ T651
Thickness: 5mm to 150mm,
Stock Size: 4 x 8; 1219 x 2438mm,1500mm x 3000mm; 1524mm x 3048mm
Produce to ASTM B209 or GB/T3880-2012, EN485 standard;
Surface: mill finish surface, bright, polished surface,
Over 3,000Tons ready stock with standard size 1524x 3048mm & 1500 x 3000mm
We can cut the corresponding size according to your needs
Cutting can be done using mechanical cutting tools such as shearing machines or cutting machines, according to the size requirements provided by the customer.
What will affect the cutting of aluminum alloy slugs？
1.Cutting process: Choosing the appropriate cutting process is crucial for obtaining high-quality aluminum plate cutting. Common cutting techniques include mechanical cutting, laser cutting, and plasma cutting. Each cutting process has its advantages and limitations. For example, laser cutting has high precision and a small heat affected zone, but may result in higher cutting costs.
2. Cutting speed: Cutting speed refers to the speed at which the cutting tool or cutting equipment moves during the cutting process. Cutting speeds that are too fast or too slow can affect cutting quality. If the cutting speed is too fast, it may cause burrs, slag residue, or uneven cutting lines on the cutting edge. On the contrary, a slow cutting speed may result in excessive heat generation during the cutting process, causing deformation of the aluminum plate or welding slag on the cutting line.
3.Material characteristics: The hardness, thickness, purity, and surface condition of aluminum plates can also affect cutting quality. Aluminum plates with higher hardness may require stronger cutting equipment and more wear-resistant cutting tools. Thicker aluminum plates may require more powerful cutting equipment to ensure cutting efficiency. Meanwhile, the flatness and smoothness of the surface state can also affect the accuracy and quality of cutting,
6061 Aluminum Plate Quality Data Sheet/Chemistry Composition:
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Single | Total | |||||||||||
7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | \ | 5.1-6.1 | 0.2 | 0.05 | 0.15 | remainder |
What is 7000 series aluminum alloy？
7xxx aluminum alloy
The main alloying element of Class 7 aluminum alloys is zinc, usually with a certain amount of copper and magnesium.
Due to the use of zinc, this type of alloy is the strongest among all forged alloys, and its strength can even exceed that of some steels.
That's why Class 7 alloys are commonly used in the aircraft industry. Although the addition of zinc can also reduce its processability, its excellent strength compensates for these drawbacks.
For example, 7075 aluminum alloy is an ideal choice for high stress parts due to its excellent weight to strength ratio. And it can be processed by molding, heat treatment and other operations as needed.
6061-T6 Aluminum Alloy Plate Mechanical Properties Standard：
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Hardness | |
|---|---|---|---|---|---|
| 7075 T6 | 525Mpa | 6 | Qualified | 157HB | |
| 7075 T651 | 540Mpa | 6 | Qualified | 160HB | |
What is 7075 T651 aluminum Sheet？
7075-T651 is known as the best product among aluminum alloys. T651 indicates that this alloy has undergone heat treatment and pre stretching processes. T6 and T651 alloys have a tensile strength of 572 MPa and a yield strength of 503 MPa. Meanwhile, 7075 alloy has excellent mechanical properties and anodizing performance. The American ASTM.
Standards Association evaluates 7075 alloy as having Class B mechanical properties due to its ability to produce curled or easily breakable chips and excellent surface treatment.
What are the applications of 7075 aluminum alloy?
When weight is a critical factor but strength cannot be compromised, the 7075 T651 aluminum plate is a widely favored alternative to steel. Alloy 7075 boasts an exceptional strength-to-weight ratio, far superior to that of steel, making it a popular choice across multiple industries. With a strength-to-weight ratio of 196 kN-m/kg, 7075 combines high strength and light weight, ideal for demanding sectors such as aviation, automotive, and firearms manufacturing.
Originally developed in 1936, 7075 was introduced as a solution to enhance aircraft fuel efficiency by reducing weight while maintaining the structural integrity required for complex maneuvers. Although it doesn't offer the same level of corrosion resistance as alloy 6061, its outstanding performance in high-stress environments, thanks to zinc being its primary alloying element, has cemented its role in the aerospace industry.
Beyond aviation, 7075 is also heavily utilized in the automotive industry for similar reasons, offering both durability and weight savings. Its strength has also made it a key material in the firearms industry, with the alloy featured in the construction of weapons like the M16, AR-15, and various handguns.
As a member of the 7000 aluminum series, 7075 is now integral to countless products in a variety of applications where high strength and reduced weight are essential.
1.How to use 7075 aluminum alloy
7075-T651 is a high-strength aluminum alloy commonly used to manufacture components that withstand high stress, such as aerospace parts, bicycle frames, etc. To ensure a flatness of 0.03 threads, precise processing techniques and equipment are required.
The following are possible processing techniques:
Precision cutting: Using high-precision CNC machine tools and rigid cutting tools, adopting a cutting method of small cutting depth, small feed rate, and low cutting speed to reduce the impact of cutting force on the workpiece and ensure flatness.
Grinding processing: High precision surface grinding machines or CNC grinding machines are used, with fine grinding wheels and coolant to control the temperature and pressure during the grinding process, ensuring grinding accuracy and flatness.
Grinding: Using grinding tools and abrasives, the surface roughness is removed through the grinding process to improve flatness.
Polishing: Using polishing cloth, polishing agent and other materials, the micro unevenness of the surface is removed by manual or mechanical polishing to improve flatness.
It should be noted that in order to ensure flatness and accuracy, the material needs to be accurately measured and calibrated before processing. During processing, environmental factors such as temperature and humidity need to be strictly controlled, and precise testing and inspection are required after processing.
2.7075 t651 Aluminum vs 7075-t7351 Aluminum
T651 is first subjected to solution treatment followed by artificial aging, and then subjected to tensile treatment to eliminate residual stress after solution treatment;
T7351 is subjected to graded aging after solution treatment, and is subjected to tensile treatment to eliminate residual stress after solution treatment. Its strength is lower than T651 and its corrosion resistance is significantly improved.