Specifications of 6082 Aluminium Sheet：
Aluminium Alloy: 6082 (Al Si1MgMn)
Temper: T6 / T651
Produce to ASTM B209 or GB/T3880-2012, EN485 standard; IS standard.
Standard size: 4 x 8; 1219 x 2438mm, 1500mm x 3000mm;
Surface: mill finish surface, bright, polished surface, with PE films to protect the surface;
Mainly market: Europe, India, Iran, Pakistan, Thailand, Mexico, USA and so on.
6082 Aluminum Plate Quality Data Sheet/Chemistry Composition:
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Single | Total | |||||||||||
6082 | 0.7- 1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6- 1.2 | 0.25 | \ | 0.2 | 0.1 | 0.05 | 0.15 | remainder |
6082-T6 Aluminum Alloy Plate Mechanical Properties Standard：
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Hardness | |
|---|---|---|---|---|---|
| 6082 T6 | 330Mpa | 6 | Qualified | Above 95HB | |
| 6082 T651 | 330Mpa | 6 | Qualified | Above 95HB | |
Aluminium Alloy 6082 T6 vs 6082 T651 ：
The T6 and T651 states of 6082 aluminum alloy differ in processing technology and performance. The T6 state undergoes artificial aging treatment after solid solution treatment, while the T651 state has an additional tensile stress relief process based on T6.
In terms of mechanical properties, 6082 aluminum alloy has high mechanical characteristics in T6 state, such as tensile strength σ b (MPa) ≥ 245, conditional yield strength σ 0.2 (MPa) ≥ 140, and elongation Δ 10 (%) ≥ 102. On the basis of T6, the T651 state further improves the stability and dimensional accuracy of the material by tensile stress relief.
In terms of processing performance, 6082 aluminum alloy has good formability and weldability in T6 state, but the strength of the welding zone will be reduced. The T651 state has a more stable processing performance due to the addition of a tensile stress relief process, making it suitable for applications with high precision requirements.
In terms of corrosion resistance, 6082 aluminum alloy exhibits good corrosion resistance and oxidation resistance in both T6 and T651 states, making it suitable for environments with high corrosion resistance requirements.
What are the applications of 6082 T6/T651 aluminum alloy?
6082 aluminum alloy is widely used in various fields such as aerospace, transportation, packaging, construction, electronics, etc.
Aerospace:
Used for manufacturing aircraft parts, landing gear, etc., due to its high strength and good weldability, it is suitable for aviation fixed devices.
Automobile manufacturing:
Used for manufacturing automotive parts, body components, and interior decorations due to its excellent corrosion resistance and machinability.
Construction industry:
Used for making window frames, door frames, exterior wall panels, etc., which not only meet the structural strength requirements but also reduce the weight of buildings.
Shipbuilding:
Used for ship accessories and hardware, suitable for fields that require high strength, weldability, and corrosion resistance.
Mechanical equipment:
Used for manufacturing various mechanical components, forgings, and structural parts due to their excellent processing characteristics and anodic reaction performance.
How to package 6082 T6/T651 aluminum plate？
Mainly including wooden pallets and export wooden box packaging. This packaging method can effectively protect the safety of aluminum materials during transportation and storage.
The packaging features of 6082-T6 aluminum include:
Packaging materials: Wooden pallets or export wooden boxes are usually used for packaging.
Protective measures: The aluminum surface will be treated with double-sided film to prevent scratching and contamination.
1.6082 Aluminum Alloy vs 6061 Aluminum Alloy
Aluminum alloys 6082 and 6061 are common engineering aluminum alloy materials, with some differences in composition, strength, and application.
Ingredients:
The main alloying elements of 6082 aluminum alloy are aluminum, silicon, magnesium, and zirconium. The addition of zirconium helps to improve the corrosion resistance and fatigue resistance of the alloy.
The main alloying elements of 6061 aluminum alloy are aluminum, magnesium, and silicon. This makes 6061 alloy have high strength and hardness.
strength:
6082 aluminum alloy has higher strength compared to 6061 alloy, especially with better strength retention performance under high temperature conditions. This makes 6082 alloy suitable for engineering structures and transportation manufacturing that require high strength and corrosion resistance.
6061 aluminum alloy also has high strength, but its strength retention performance at high temperatures is relatively poor.
Application:
6082 aluminum alloy is commonly used in engineering structures that require high strength and corrosion resistance, such as aerospace components, railway vehicles, and trucks.
6061 aluminum alloy is suitable for applications that require high strength and corrosion resistance, such as aircraft components, automotive parts, and ship components.
2.What is T6 in Aluminium alloy?
T6 in aluminum alloy is a heat-treated state, corresponding to Temperature 6 in English. This state of aluminum alloy has high strength and hardness, as well as good plasticity, toughness, and corrosion resistance. T6 treated aluminum alloys are commonly used to manufacture parts that require high strength, such as those in the automotive, aircraft, aerospace, and other fields.
T6 tunnel type heat treatment furnace
The T6 heat treatment process includes two main steps: solution treatment and artificial aging. Solution treatment is the process of heating aluminum alloy to a certain temperature (usually between 500-600 degrees Celsius), holding it for a certain period of time, and then rapidly cooling it. This process can cause some phases in aluminum alloys to change, forming more stable phases, thereby improving the strength and hardness of the alloy. Artificial aging is the process of holding the solution treated aluminum alloy at a certain temperature for a period of time to further enhance its properties.
The specific parameters of T6 heat treatment process, such as solution temperature, quenching rate, aging temperature, holding time, and aging stages, will vary depending on the composition of different alloys. For different alloys, even with the same heat treatment code T6, the values of these factors may vary. Therefore, the T6 heat treatment process needs to be adjusted according to the specific alloy composition to achieve the best mechanical properties
3.Is 6082 T6 bendable?
6082-T6 aluminum alloy can be bent. 6082-T6 aluminum alloy has good plasticity and is suitable for cold forming operations such as bending, stamping, and deep drawing, especially for making thin-walled structures or complex shapes.
6082 T6 aluminum profile
The processing performance of 6082-T6 aluminum alloy is excellent. It can be used for various processing operations such as cutting, drilling, milling, bending, etc., and it is not easy to produce cracks during the processing, making it suitable for complex component manufacturing.
In addition, 6082-T6 aluminum alloy also has high strength and good corrosion resistance. After T6 heat treatment, its strength and hardness are significantly improved, and it can be used for a long time in harsh environments without being easily damaged.
Are you looking for a 6082 aluminum sheet supplier in China? Contact with Yantai Edobo Aluminum Co.,Ltd, we will start a long-term business cooperation by this chance.
Specifications of 6082 Aluminium Sheet：
Aluminium Alloy: 6082 (Al Si1MgMn)
Temper: T6 / T651
Produce to ASTM B209 or GB/T3880-2012, EN485 standard; IS standard.
Standard size: 4 x 8; 1219 x 2438mm, 1500mm x 3000mm;
Surface: mill finish surface, bright, polished surface, with PE films to protect the surface;
Mainly market: Europe, India, Iran, Pakistan, Thailand, Mexico, USA and so on.
6082 Aluminum Plate Quality Data Sheet/Chemistry Composition:
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Single | Total | |||||||||||
6082 | 0.7- 1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6- 1.2 | 0.25 | \ | 0.2 | 0.1 | 0.05 | 0.15 | remainder |
6082-T6 Aluminum Alloy Plate Mechanical Properties Standard：
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Hardness | |
|---|---|---|---|---|---|
| 6082 T6 | 330Mpa | 6 | Qualified | Above 95HB | |
| 6082 T651 | 330Mpa | 6 | Qualified | Above 95HB | |
Aluminium Alloy 6082 T6 vs 6082 T651 ：
The T6 and T651 states of 6082 aluminum alloy differ in processing technology and performance. The T6 state undergoes artificial aging treatment after solid solution treatment, while the T651 state has an additional tensile stress relief process based on T6.
In terms of mechanical properties, 6082 aluminum alloy has high mechanical characteristics in T6 state, such as tensile strength σ b (MPa) ≥ 245, conditional yield strength σ 0.2 (MPa) ≥ 140, and elongation Δ 10 (%) ≥ 102. On the basis of T6, the T651 state further improves the stability and dimensional accuracy of the material by tensile stress relief.
In terms of processing performance, 6082 aluminum alloy has good formability and weldability in T6 state, but the strength of the welding zone will be reduced. The T651 state has a more stable processing performance due to the addition of a tensile stress relief process, making it suitable for applications with high precision requirements.
In terms of corrosion resistance, 6082 aluminum alloy exhibits good corrosion resistance and oxidation resistance in both T6 and T651 states, making it suitable for environments with high corrosion resistance requirements.
What are the applications of 6082 T6/T651 aluminum alloy?
6082 aluminum alloy is widely used in various fields such as aerospace, transportation, packaging, construction, electronics, etc.
Aerospace:
Used for manufacturing aircraft parts, landing gear, etc., due to its high strength and good weldability, it is suitable for aviation fixed devices.
Automobile manufacturing:
Used for manufacturing automotive parts, body components, and interior decorations due to its excellent corrosion resistance and machinability.
Construction industry:
Used for making window frames, door frames, exterior wall panels, etc., which not only meet the structural strength requirements but also reduce the weight of buildings.
Shipbuilding:
Used for ship accessories and hardware, suitable for fields that require high strength, weldability, and corrosion resistance.
Mechanical equipment:
Used for manufacturing various mechanical components, forgings, and structural parts due to their excellent processing characteristics and anodic reaction performance.
How to package 6082 T6/T651 aluminum plate？
Mainly including wooden pallets and export wooden box packaging. This packaging method can effectively protect the safety of aluminum materials during transportation and storage.
The packaging features of 6082-T6 aluminum include:
Packaging materials: Wooden pallets or export wooden boxes are usually used for packaging.
Protective measures: The aluminum surface will be treated with double-sided film to prevent scratching and contamination.
1.6082 Aluminum Alloy vs 6061 Aluminum Alloy
Aluminum alloys 6082 and 6061 are common engineering aluminum alloy materials, with some differences in composition, strength, and application.
Ingredients:
The main alloying elements of 6082 aluminum alloy are aluminum, silicon, magnesium, and zirconium. The addition of zirconium helps to improve the corrosion resistance and fatigue resistance of the alloy.
The main alloying elements of 6061 aluminum alloy are aluminum, magnesium, and silicon. This makes 6061 alloy have high strength and hardness.
strength:
6082 aluminum alloy has higher strength compared to 6061 alloy, especially with better strength retention performance under high temperature conditions. This makes 6082 alloy suitable for engineering structures and transportation manufacturing that require high strength and corrosion resistance.
6061 aluminum alloy also has high strength, but its strength retention performance at high temperatures is relatively poor.
Application:
6082 aluminum alloy is commonly used in engineering structures that require high strength and corrosion resistance, such as aerospace components, railway vehicles, and trucks.
6061 aluminum alloy is suitable for applications that require high strength and corrosion resistance, such as aircraft components, automotive parts, and ship components.
2.What is T6 in Aluminium alloy?
T6 in aluminum alloy is a heat-treated state, corresponding to Temperature 6 in English. This state of aluminum alloy has high strength and hardness, as well as good plasticity, toughness, and corrosion resistance. T6 treated aluminum alloys are commonly used to manufacture parts that require high strength, such as those in the automotive, aircraft, aerospace, and other fields.
T6 tunnel type heat treatment furnace
The T6 heat treatment process includes two main steps: solution treatment and artificial aging. Solution treatment is the process of heating aluminum alloy to a certain temperature (usually between 500-600 degrees Celsius), holding it for a certain period of time, and then rapidly cooling it. This process can cause some phases in aluminum alloys to change, forming more stable phases, thereby improving the strength and hardness of the alloy. Artificial aging is the process of holding the solution treated aluminum alloy at a certain temperature for a period of time to further enhance its properties.
The specific parameters of T6 heat treatment process, such as solution temperature, quenching rate, aging temperature, holding time, and aging stages, will vary depending on the composition of different alloys. For different alloys, even with the same heat treatment code T6, the values of these factors may vary. Therefore, the T6 heat treatment process needs to be adjusted according to the specific alloy composition to achieve the best mechanical properties
3.Is 6082 T6 bendable?
6082-T6 aluminum alloy can be bent. 6082-T6 aluminum alloy has good plasticity and is suitable for cold forming operations such as bending, stamping, and deep drawing, especially for making thin-walled structures or complex shapes.
6082 T6 aluminum profile
The processing performance of 6082-T6 aluminum alloy is excellent. It can be used for various processing operations such as cutting, drilling, milling, bending, etc., and it is not easy to produce cracks during the processing, making it suitable for complex component manufacturing.
In addition, 6082-T6 aluminum alloy also has high strength and good corrosion resistance. After T6 heat treatment, its strength and hardness are significantly improved, and it can be used for a long time in harsh environments without being easily damaged.