Specification | ||||||||||||
Alloy: 5052, 5005, 5754, 5083 etc. | ||||||||||||
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc. | ||||||||||||
Thickness: 0.2-200mm | ||||||||||||
Width: Up to 1800mm | ||||||||||||
Length: up to 6000mm | ||||||||||||
Surface treatment: mill finished, PVC coated, Print marks | ||||||||||||
Feature | Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry. | |||||||||||
Forming: It is readily formed at room temperature. Successive cold working decreases the formability. | ||||||||||||
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working. | ||||||||||||
Forging: It may be forged in the temperature range of 950 F down to 500 F | ||||||||||||
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary. | ||||||||||||
Annealing: Anneal at 650 F and air cool. | ||||||||||||
Hardening: Hardens only from cold working. | ||||||||||||
Application | hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc. | |||||||||||
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | others | Al | ||
single | total | |||||||||||
5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.3 | \ | 0.1 | \ | 0.05 | 0.15 | remainder |
5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | \ | 0.25 | \ | 0.05 | 0.15 | remainder |
5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | \ | 0.2 | 0.15 | 0.05 | 0.15 | remainder |
5083 | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | \ | 0.25 | 0.15 | 0.05 | 0.15 | remainder |
Specification | ||||||||||||
Alloy: 5052, 5005, 5754, 5083 etc. | ||||||||||||
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc. | ||||||||||||
Thickness: 0.2-200mm | ||||||||||||
Width: Up to 1800mm | ||||||||||||
Length: up to 6000mm | ||||||||||||
Surface treatment: mill finished, PVC coated, Print marks | ||||||||||||
Feature | Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry. | |||||||||||
Forming: It is readily formed at room temperature. Successive cold working decreases the formability. | ||||||||||||
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working. | ||||||||||||
Forging: It may be forged in the temperature range of 950 F down to 500 F | ||||||||||||
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary. | ||||||||||||
Annealing: Anneal at 650 F and air cool. | ||||||||||||
Hardening: Hardens only from cold working. | ||||||||||||
Application | hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc. | |||||||||||
Alloy | Chemical Component %≤ | |||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | others | Al | ||
single | total | |||||||||||
5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.3 | \ | 0.1 | \ | 0.05 | 0.15 | remainder |
5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | \ | 0.25 | \ | 0.05 | 0.15 | remainder |
5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | \ | 0.2 | 0.15 | 0.05 | 0.15 | remainder |
5083 | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | \ | 0.25 | 0.15 | 0.05 | 0.15 | remainder |
What is 6061-T6 Aluminum Used For? Aluminum is a versatile material used in a variety of industries due to its lightweight and durable properties. Among the different types of aluminum, 6061-T6 aluminum stands out for its exceptional strength and versatility. This article delves into the various ap
Understanding the Differences Between 3003 and 5005 Aluminum Aluminum alloys are widely used in various industries due to their excellent properties, such as lightweight, corrosion resistance, and high strength. Among the numerous aluminum alloys available, 3003 and 5005 aluminum alloys are two of
Aluminum is a versatile material that is used in a wide range of industries, from aerospace to automotive to construction. One of the most popular aluminum alloys is 2024, which is known for its high strength and excellent machinability. Within the 2024 alloy family, two of the most common tempers a
6061-T6 temper: After xrlutian treatment, it is cooled to achieve high strength and no longer subjected to cold processing; 6061-T651 temper: After xrlutian treatment, it is cooled to achieve high strength, and then cold stretched by a stretching machine to eliminate residual internal stress after heat treatment, achieving no deformation after deep processing to ensure the precision of machined products.
The common states of 6061 aluminum plate include O state, T4 state, T6 state, and T651 state. The T651 state alloy is formed by stretching on the basis of T6 state to eliminate internal stress, making it more suitable for processing and forming.The difference between T6 and T651 states of 6061 alumi